High alumina new type slag retaining plate

Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...

High-alumina new type ulter thin flow steel launder

Product Introduction Service Conditions: Overall preheating by 8~10 hours at 1000℃ Casting Capacity: Have the ability to withstand erosion-corrosion by 4,000 KGS molten steel Casting Steel Grade: Cobalt, Chromium, Nickel-based Super Alloy Casting ...

Crucible with special coating

Specifications Item/Spcs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K ...

High alumina new type pouring cup

Specifications Item/Spcs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K ...

High alumina new type quarl

Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K...

High alumina new type shunt

Product Introduction Apply to Super Alloy casting, no cracking, peeling off, chip dropping Service Temperature: room temp. ~ 1650℃； Preheating by 2~4 hours at 550~600℃ Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7...