Zirconia filter
Property Index Hole density: 8-40PPI Through rate: 80%-90% Maximum service temperature: 1750℃ Ambient Bending Strength: 0.8-1.0Mpa Ambient Compression Strength: 1.0-1.2Mpa Thermal shock resistance: Six times(1100℃) Adaptive: alloy steel,carbon...
Aluminium oxide filter
Property Index Hole density: 8-60PPI Through rate : 80%-90% maximum service temperature : 1100℃ Ambient Bending Strength : 0.6 Mpa Ambient Compression Strength: 0.8Mpa Thermal shock resistance : Six times(1100℃) Adaptive : Aluminium alloy, Nonfe...
Magnesium oxide filter
Property Index Hole density: 8-20PPI Through rate : 80%-90% maximum service temperature : Greater than 1200℃ Ambient Bending Strength : 0.7 Mpa Ambient Compression Strength: 0.8Mpa Thermal shock resistance : Four times(1100℃) Adaptive : Magnesi...
Silicon carbide filter
Property Index Hole density: 8-60PPI Through rate : 80%-90% maximum service temperature : 1500℃ Ambient Bending Strength : 0.8 Mpa Ambient Compression Strength: 0.9Mpa Thermal shock resistance : Six times(1100℃) Adaptive : Nodular cast iron,gray...
High alumina new type slag retaining plate
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
High-alumina new type ulter thin flow steel launder
Product Introduction Service Conditions: Overall preheating by 8~10 hours at 1000℃ Casting Capacity: Have the ability to withstand erosion-corrosion by 4,000 KGS molten steel Casting Steel Grade: Cobalt, Chromium, Nickel-based Super Alloy Casting ...
Crucible with special coating
Specifications Item/Spcs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K ...
High alumina new type pouring cup
Specifications Item/Spcs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K ...
High alumina new type quarl
Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K...
High alumina new type shunt
Product Introduction Apply to Super Alloy casting, no cracking, peeling off, chip dropping Service Temperature: room temp. ~ 1650℃； Preheating by 2~4 hours at 550~600℃ Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7...
High alumina new type shunt
Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K...
High alumina new type shunt
Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K...
Tapping nozzle of flow steel launder
Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K...
High alumina new type tundish
Product Introduction Apply to Super Alloy casting, no cracking, peeling off, chip dropping Service Temperature: room temp. ~ 1650℃； Preheating by 2~4 hours at 550~600℃ Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7...
High alumina new type tundish
Product Introduction Apply to Super Alloy casting, no cracking, peeling off, chip dropping Service Temperature: room temp. ~ 1650℃； Preheating by 2~4 hours at 550~600℃ Specifications Item/Specs Conditions Value (Typical) Bending Strength Span 120mm 7...
High alumina new type gap bridge
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
High alumina new type shunt
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
High alumina new type tundish
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
High alumina new type bottom mat
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
High alumina new type tapping nozzle
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
Zirconia filter
Property Index Hole density: 8-40PPI Through rate: 80%-90% Maximum service temperature: 1750℃ Ambient Bending Strength: 0.8-1.0Mpa Ambient Compression Strength: 1.0-1.2Mpa Thermal shock resistance: Six times(1100℃) Adaptive: alloy steel,carbon...
Aluminium oxide filter
Property Index Hole density: 8-60PPI Through rate : 80%-90% maximum service temperature : 1100℃ Ambient Bending Strength : 0.6 Mpa Ambient Compression Strength: 0.8Mpa Thermal shock resistance : Six times(1100℃) Adaptive : Aluminium alloy, Nonfe...
Magnesium oxide filter
Property Index Hole density: 8-20PPI Through rate : 80%-90% maximum service temperature : Greater than 1200℃ Ambient Bending Strength : 0.7 Mpa Ambient Compression Strength: 0.8Mpa Thermal shock resistance : Four times(1100℃) Adaptive : Magnesi...
Silicon carbide filter
Property Index Hole density: 8-60PPI Through rate : 80%-90% maximum service temperature : 1500℃ Ambient Bending Strength : 0.8 Mpa Ambient Compression Strength: 0.9Mpa Thermal shock resistance : Six times(1100℃) Adaptive : Nodular cast iron,gray...
High alumina new type slag retaining plate
Product Introduction Bending Condition: span 120mm Height 25mm Thickness 25mm Loading Speed: 10mm/min Bending Strength: 7.37Mpa Compression Condition: Diameter 84mm Loading Speed: 10mm/min Compression Condition: 17MPa Thermal Conductivity: Roo...
High-alumina new type ulter thin flow steel launder
Product Introduction Service Conditions: Overall preheating by 8~10 hours at 1000℃ Casting Capacity: Have the ability to withstand erosion-corrosion by 4,000 KGS molten steel Casting Steel Grade: Cobalt, Chromium, Nickel-based Super Alloy Casting ...
Crucible with special coating
Specifications Item/Spcs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K ...
High alumina new type pouring cup
Specifications Item/Spcs Conditions Value (Typical) Bending Strength Span 120mm 7.37 MPa Height 25mm Thickness 25mm loading speed Compression Strength Diameter 84mm 17 MPa Loading Speed 10mm/min Thermal Conductivity Room Temperature 0.48873 W/m·K ...
Please Leave Your Message Here
The company produces new-type Pouring System including ultra-thin Launder, Tundish, Shunt, Steel Frame etc.
Navigation
Home
About Us
Products
Service
News
Contact Us
Products
Casting Launder
Crucible
Pouring Cup
Quarl
Shunt
Tapping Nozzle
Tundish
Bottom Mat
Slag Retaining Plate
Filter